Used for filling minute pinholes and cracks in marble and granite
Step 1 : Crack Filling
Step 2 : Take resin & hardener in the 100:25 ratio, mix thoroughly and take it in dispensing bottle, dispense the mix over the crack
Step 3 : Mix will cure in 24-30 hours after that polishing can be done on that marble
Step 4 : Micro Crack Treatment
Step 5 : Take resin & hardener in above mentioned ratio, mix thoroughly and apply over the surface with the help of spatula.
Step 6 : If required, epoxy thinner can be added for further reduction in viscosity.Polishing of marble can be done only after 24-30 hours.
Step 7 : Polishing of marble can be done only after 24-30 hours.
Transparent in appearance
Low viscosity material
Water-resistant
Fast-setting
Crackbond HCF-351 is a modified epoxy system used for filling very fine micro cracks on marble surfaces.
It is designed for marble and granite, suitable for repairing minute pinholes and cracks.
Mix resin and hardener in a 100:50 ratio, dispense over the crack or apply with a spatula, and thin with epoxy thinner if needed.
The mix cures in 24-30 hours, after which the marble surface can be polished.
It is commonly used for filling minute pinholes and cracks in marble and granite surfaces.
Crackbond HCF-351 is water-resistant; heat resistance is upto 90 deg C
Avoid using Crackbond HCF-351 on dusty, oily or unclean marble surfaces, as a clean area is needed for proper filling.
Common mistakes include polishing before the full 24-30 hour cure time and not following the correct 100:50 resin-hardener ratio.
Crackbond HCF-351 is transparent, fast-setting and low viscosity, ideal for precise fine crack repair on marble.
Store Crackbond HCF-351 in a dry place in its original, properly closed container at 2-40°C, and reseal partially used containers immediately.
Shelf Life: 2 years from date of mfd. (Storage Temp 2-40°C)
Storage: Product should be stored in a dry place in their original, properly closed containers at temperature between 2-40°C. Partially emptied container should be closed immediately.
Excellent Crack-Filling in Marbles
High Gloss
Ideal Working Time
Low Viscosity